Uploads from Wolfgang Moersch, tagged palladiotype

Breitenbach, über den Ollen

nobody@flickr.com (Wolfgang Moersch) — Sat, 11 Aug 2012 14:18:57 -0700

Palladiotype 212x244mm on Arches Platine

view on black

Early Morning at the Pond, Palladiotype

nobody@flickr.com (Wolfgang Moersch) — Mon, 09 Jul 2012 06:56:31 -0700

The end of a morning walk around the Fischenich Pond
Holga 120N, RPX 100 in Tanol 5+5+500 20°C 10 minutes
printnegative 21x21cm on Wephota FO5 by reversal development
1st developer SE6 Blue 1+20 - bichromate bleach - 2nd developer Finol 3+3+300 ml
negative masked with Regumask rubyrot 63

Finally one of my favoured combinations, Palladiotype on Kozo paper.
Palladium with some drops of Sodium Platinate
developed in warm (38°C) oxalate/phosphate-developer
clearing bathes: Phosphoric acid and EDTA/Sulfite

4x5 Pond, Palladiotype

nobody@flickr.com (Wolfgang Moersch) — Wed, 04 Jul 2012 14:51:59 -0700

Wolfgang Moersch posted a photo:

Believe it or not, the original intention was to use the Holga just as a notebook. That´s why I went back one day later, very early in the morning with a large format camera.

FP4 in Tanol 2+2+200ml 12 mins at about 22°C
Palladiotype (POP) from the 4x5 camera negative on Bergger Cot-320

Palladiotype, Kozo

nobody@flickr.com (Wolfgang Moersch) — Sat, 02 Jun 2012 15:01:33 -0700

Wolfgang Moersch posted a photo:

Holga/Efke
Wephota FO5 21x21cm by reversal development
paper: Kozo
developer: Ammonium oxalate/Potassium oxalate with 10 drops Sodium bichromate 50% per litre
clearing bath: EDTA4Na/Sodium sulfite

altprocess stuff - five other examples for paper comparison
perhaps just interesting for alternative printers

Palladiotype on a new batch of Arches Platine

Kallitypes on
Kozo
Bergger Cot-320
Arches Platine
Arches Platine toned

Silica Coating Test #4 Palladium

nobody@flickr.com (Wolfgang Moersch) — Wed, 18 Apr 2012 23:45:27 -0700

Wolfgang Moersch posted a photo:

Palladiotypes from the original 4x5 negative - the print on the right hand side is silica coated - same treatment apart from that.
Linhof 90mm, TMY in Tanol Speed
view large, original size for comparison

Silica Coating Test #1 Palladium

nobody@flickr.com (Wolfgang Moersch) — Thu, 23 Feb 2012 11:29:15 -0800

Wolfgang Moersch posted a photo:

Holga 120N, Delta 400 in Finol
printnegative on Wephota FO5 23,5x25,5cm
Bergger Cot-320 coated with Silica
Palladiotype (traditional developing process)
masked with Regumask rubyrot 63
developer Oxalate/Phosphate
clearing 3 baths of Phosphoric acid 4% - without a wash after developing
I found that it is impossible to remove the iron stain completly with this paper (contrary to Arches Platine), when a water rinse was made before the clearing bath.

Precoating with Silica causes an increase of contrast and dmax.

WARNING
Take care with the dust of Fumed Silica. Breathing in of the fine dust particles can be hazardous to health.

Anthurium Pd

nobody@flickr.com (Wolfgang Moersch) — Wed, 15 Feb 2012 00:02:32 -0800

Wolfgang Moersch posted a photo:

printed 2012
Palladiotype on Weston Diploma Parchment

Lith print for comparison

Palladium POP Ware

nobody@flickr.com (Wolfgang Moersch) — Wed, 28 Dec 2011 08:22:58 -0800

Wolfgang Moersch posted a photo:

Hasselblad Planar 80mm, Plus-X rated at 400 ASA, developed in eco film developer
enlarged negative on Wephota FO5 28x32cm by reversal development
Ammonium Palladium (Ware process) on Bergger Cot-320

for comparison Ziatype

Am Teichufer

nobody@flickr.com (Wolfgang Moersch) — Mon, 02 Jul 2012 00:58:25 -0700

Wolfgang Moersch posted a photo:

Holga 120N, Efke IR820, eco film developer 2+1+50 11 Minuten
Drucknegativ auf Wephota FO5, Umkehrentwicklung in SE6 Blue 1+20
Palladiotype Mike Ware´s Ammonium-Palladium Auskopierverfahren (60% rel. Luftfeuchtigkeit) auf Arches Platine
Bildrand maskiert mit Regumask rubyrot 63
nach der Belichtung direkt ins Klärbad
EDTA2Na 20 Minuten und EDTA4Na/Sulfit 10 Minuten

Palladiotype, Arches

nobody@flickr.com (Wolfgang Moersch) — Sat, 02 Jun 2012 14:59:30 -0700

Wolfgang Moersch posted a photo:

Holga/Efke
Wephota FO5 21x21cm by reversal development
paper: Arches Platine
developer: Ammonium oxalate/Potassium oxalate with 10 drops Sodium bichromate 50% per litre
clearing bath: EDTA4Na/Sodium sulfite

Downy Birch, Palladium

nobody@flickr.com (Wolfgang Moersch) — Fri, 30 Mar 2012 09:27:19 -0700

Wolfgang Moersch posted a photo:

Palladiotype 38x38cm on Bergger Cot-320

Kaltbrunnental, Palladiotype

nobody@flickr.com (Wolfgang Moersch) — Thu, 09 Feb 2012 16:02:15 -0800

Wolfgang Moersch posted a photo:

One more view of Kaltbrunnental, taken summer 2003
Linhof Technikardan, Schneider Super Angulon 120mm, Efke IR820 4x5 in MZB, filter dark red (R29)
enlarged on Wephota FO5 by reversal development 25x32,5cm
the negative is a bit too contrasty for palladium (loss of shadow detail), instead to make a new one I tried it with the softer working Ziatype

Kaltbrunnental

nobody@flickr.com (Wolfgang Moersch) — Mon, 06 Feb 2012 08:31:46 -0800

Wolfgang Moersch posted a photo:

Manche Negative sind nur mit Geduld und Aufwand auf Papier zu bringen. Dieses ist eins von der Sorte. Früher hätte ich es frustriert in den Müll geschmissen, doch mit der Zeit wird man klüger und legt es einfach beiseite, in der Hoffnung, eines Tages in guter Form die notwendigen Register ziehen zu können.
In das schöne Kaltbrunnental habe ich mich schon oft abgeseilt, wenn der heiße Schweizer Sommer nur die Alternative Pool oder Wald zuließ. An dieser Stelle verengt sich das Tal zu einer Schlucht, nur zur Mittagszeit erreichen einige Sonnenstrahlen den Boden. Es ist dort wohltuend kühl und feucht und - ziemlich duster am Grund, flirrend hell in den oberen Etagen. "Geht nicht" sagt der Spotmeter, paßt schon, meint der ignorante Operateur.
Die Verwendung eines IR-Films bringt den Vorteil einer deutlichen Aufhellung der begrünten Schatten, doch der Kontrast zu den Hochlichtern bleibt hoch, eine IR-typische Überstrahlung der Lichter mußte vermieden werden. Also war eine möglichst knappe Belichtung angebracht, was wiederum ein Vorgehen nach dem Zonensystem ausschloß. Schon wegen der notwendigen mittleren Blendenöffung für das 4x5 Format lag die Belichtungszeit auch ohne eine Verlängerung für N- im Grenzbereich, denn in den oberen Etagen gab es eine leichte Luftbewegung.
Efke IR820 - ein 25iger Rotfilter reichte für den Zweck aus. Entwickelt wurde im MZB. Das Negativ hat sehr gute Schattenzeichnung, doch trotz Ausgleichsentwicklung liegen die Lichter zu hoch.
Um die Schatten bei der benötigten Belichtungszeit für die Lichter zu halten, wurde eine zarte Silbermaske erstellt und im Sandwich auf Wephota FO5 Film vergrößert.

Palladiotypie auf Bergger Cot-320 22,5x26,5cm
roter Maskierungsfilm für den Bildrand

Was bei einem belichteten Rand nicht auffällt, ist eine nicht völlige Klärung des Eisensalzes durch Zitronensäure und EDTA/Sulfit beim Cot-320. Ein Vergleichsprint auf Arches Platine zeigte nach der gleichen Behandlung keine Rückstände in den Weißen.
Wie es scheint, entstehen bei einigen Papieren schwer lösbare Verbindungen, wenn nach Oxalatentwicklern ein Wasserbad vor dem Klärbad eingeschoben wird. Verzichtet man auf den Spülgang nach der Entwicklung und klärt sofort in Phosphorsäure, verschwindet der Bildrand-Gilb auch beim Cot-320 vollständig.

Palladium POP Ziatype

nobody@flickr.com (Wolfgang Moersch) — Wed, 28 Dec 2011 08:28:02 -0800

Wolfgang Moersch posted a photo:

Hasselblad Planar 80mm, Plus-X rated at 400 ASA, developed in eco film developer
enlarged negative on Wephota FO5 28x32cm by reversal development
Ziatype on Bergger Cot-320
Ammonium Ferric Oxalate 1,5ml + Lithium Palladium 1,2ml + Gold Chloride 5% 0,3ml

for comparison Mike Ware´s POP

carpe noctem...

nobody@flickr.com (Wolfgang Moersch) — Fri, 23 Dec 2011 10:22:02 -0800

Wolfgang Moersch posted a photo:

und geh in die Kammer - got to the red light sphere, if you have nothing better to do
Palladium POP (Ware process) 28x28cm on Bergger Cot-320
Sometimes I had problems with this process in the past. Now I found out that it just was a wrong (too soft) brush.